Identification of the C2∏-X2Σ+ band system of AlO in the ultraviolet galvanoluminescence obtained during aluminum anodization

Abstract

The first galvanoluminescence spectrum in the ultraviolet region obtained during anodization of high purity aluminum samples annealed at temperature above 525°C is presented. An intense broad peak with the maximum at about 31,900 cm(-1) is assigned to the transitions (some of them heretofore unobserved) between vibrational levels of the C(2)∏→X(2)Σ(+) spectral system of AlO, partly overlapped with the A(2)Σ(+)→X(2)∏ system of OH.